Temperature-dependent analysis of conduction mechanism of leakage current in thermally grown oxide on 4H-SiC

Abstract

The conduction mechanism of the leakage current of a thermally grown oxide on 4H silicon carbide (4H-SiC) was investigated. The dominant carriers of the leakage current were found to be electrons by the carrier-separation current-voltage method. The current-voltage and capacitance-voltage characteristics, which were measured over a wide temperature range, revealed that the leakage current in SiO2/4H-SiC on the Si-face can be explained as the sum of the Fowler-Nordheim (FN) tunneling and Poole-Frenkel (PF) emission leakage currents. A rigorous FN analysis provided the true barrier height for the SiO2/4H-SiC interface. On the basis of Arrhenius plots of the PF current separated from the total leakage current, the existence of carbon-related defects and/or oxygen vacancy defects was suggested in thermally grown SiO2 films on the Si-face of 4H-SiC.