Mechanical properties of potato starch modified by moisture content and addition of lubricant

Abstract

Abstract Laboratory testing was conducted to deliver a set of characteristics of structure and mechanical properties of pure starch and starch with an addition of a lubricant - magnesium stearate. Considerable influence of moisture content of potato starch was found in the case of density, parameters of internal friction, coefficients of wall friction and flowability. Elasticity was found to be strongly influenced by water content of the material. Addition of magnesium stearate affected density and parameters of flowability, internal friction and elasticity. Bulk density increased from 604 to 774 kg m -3 with decrease in moisture content of potato starch from 17 to for 6%. Addition of magnesium stearate resulted in approximately 10% decrease in bulk density. Angle of internal friction obtained for 10 kPa of consolidation stress decreased from 33 to 24º with increase in moisture content, and to approximately 22º with addition of the lubricant. With an increase of moisture content from 6 to 18% and with addition of the lubricant, the modulus of elasticity during loading decreased from approximately 1.0 to 0.1 MPa. Modulus of elasticity during unloading was found in the range from 19 to 42 MPa and increased with increase of moisture content and amount of lubricant.