on-Resistance Degradation Induced by Hot-Carrier Injection in SOI SJ-LDMOS

Abstract

In this brief, anomalous hot-carrier degradation phenomenon in n-type superjunction lateral DMOS transistors on a SOI substrate is investigated. An unexpected on-resistance ( <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">R</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> ) decrease was observed at the beginning of stress, but <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">R</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> increases with the stress time. The reason was analyzed with the 3-D simulation of electrical field and impact ionization generation. The injection of hot holes into the field oxide near the drain region leads to the <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">R</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> decrease during the early stress period. With the increase of stress time, trapped hot holes accumulated in the field oxide and act as electron defects to trap electrons, altogether with hot electrons trapped in gate oxide above the accumulation region, contributing to <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">R</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">on</sub> increase.