Diamond field effect transistors with a high-dielectric constant Ta₂O₅as gate material

Abstract

A Ta2O5/Al2O3 bilayer gate oxide with a high-dielectric constant (high-k) has been successfully applied to a hydrogenated-diamond (H-diamond) metal-insulator-semiconductor field effect transistor (MISFET). The Ta2O5 layer is prepared by a sputtering-deposition (SD) technique on the Al2O3 buffer layer fabricated by an atomic layer deposition (ALD) technique. The ALD-Al2O3 plays an important role to eliminate plasma damage for the H-diamond surface during SD-Ta2O5 deposition. The dielectric constants of the SD-Ta2O5/ALD-Al2O3 bilayer and single SD-Ta2O5 are as large as 12.7 and 16.5, respectively. The k value of the single SD-Ta2O5 in this study is in good agreement with that of the SD-Ta2O5 on oxygen-terminated diamond. The capacitance–voltage characteristic suggests low interfacial trapped charge density for the SD-Ta2O5/ALD-Al2O3/H-diamond MIS diode. The MISFET with a gate length of 4 µm has a drain current maximum and an extrinsic transconductance of −97.7 mA mm−1 (normalized by gate width) and 31.0 ± 0.1 mS mm−1, respectively. The effective mobility in the H-diamond channel layer is found to be 70.1 ± 0.5 cm2 V−1 s−1.