Silicate Reaction Control at Lanthanum Oxide and Silicon Interface for Equivalent Oxide Thickness of 0.5 nm: Adjustment of Amount of Residual Oxygen Atoms in Metal Layer

Abstract

A guideline to select appropriate gate electrode materials to achieve an equivalent oxide thickness (EOT) of 0.5 nm with La 2 O 3 gate dielectric has been proposed. The key parameter includes the adjustment of the amount of supplied oxygen atoms, which trigger the formation of the silicate layer at the interface, by selecting a metal with moderate free energy of oxygen. In addition, the thickness of the metal gate has been found to play an important role in silicate formation. Based on this guideline, an EOT of 0.5 nm with 3.5 nm La 2 O 3 and 6 nm W gate electrode annealed at 800 °C was achieved. The hysteresis and humps in the capacitance voltage characteristics have been explained by the defect energy levels in the formed silicates and located at the interface with La 2 O 3 . The flat-band voltage shift correlated with the thickness of the oxygen-containing metal indicates the existence of fixed charges induced by the gate electrode metal. Finally, an appropriate transistor operation at an EOT of 0.5 nm has been confirmed.