Origin of the n-type conductivity of InN: The role of positively charged dislocations

Abstract

As-grown InN is known to exhibit high unintentional n-type conductivity. Hall measurements from a range of high-quality single-crystalline epitaxially grown InN films reveal a dramatic reduction in the electron density (from low 1019 to low 1017cm−3) with increasing film thickness (from 50to12000nm). The combination of background donors from impurities and the extreme electron accumulation at InN surfaces is shown to be insufficient to reproduce the measured film thickness dependence of the free-electron density. When positively charged nitrogen vacancies (VN+) along dislocations are also included, agreement is obtained between the calculated and experimental thickness dependence of the free-electron concentration.