Defect-driven inhomogeneities in Ni∕4H–SiC Schottky barriers

Abstract

Nanoscale depth-resolved cathodoluminescence spectroscopy (DRCLS) of Ni diode arrays on 4H-SiC epitaxial wafers reveals a striking correspondence between deep level defects and electrical transport measurements on a diode-by-diode basis. Current-voltage measurements display both ideal and nonideal diode characteristics due to multiple barriers within individual contacts. Near-interface DRCLS demonstrates the presence of three discrete midgap defect levels with 2.2, 2.45, and 2.65eV emission energies whose concentrations vary on a submicron scale among and within individual diodes, correlating with barrier inhomogeneity. These results also suggest that SiC native defect levels can account for the maximum range of n-type barrier heights.