Ultrafast electroabsorption dynamics in an InAs quantum dot saturable absorber at 1.3μm

Abstract

The authors report a direct measurement of the absorption dynamics in an InAs p-i-n ridge waveguide quantum dot modulator. The carrier escape mechanisms are investigated via subpicosecond pump-probe measurements at room temperature, under reverse bias conditions. The optical pulses employed are degenerate in wavelength with the quantum dot ground state transition at 1.28μm. The absorption change recovers with characteristic times ranging from 62ps (0V)to∼700fs (−10V), showing a decrease of nearly two orders of magnitude. The authors show that at low applied fields, this recovery is attributed to thermionic emission while for higher applied fields, tunneling becomes the dominant mechanism.