Study on β-Ga2O3 Films Grown with Various VI/III Ratios by MOCVD

Abstract

β-Ga2O3 films were grown on sapphire (0001) substrates with various O/Ga (VI/III) ratios by metal organic chemical vapor deposition. The effects of VI/III ratio on growth rate, structural, morphological, and Raman properties of the films were systematically studied. By varying the VI/III ratio, the crystalline quality obviously changed. By decreasing the VI/III ratio from 66.9 × 103 to 11.2 × 103, the crystalline quality improved gradually, which was attributed to low nuclei density in the initial stage. However, crystalline quality degraded with further decrease of the VI/III ratio, which was attributed to excessive nucleation rate.