Effect of film thickness on the ferroelectric and dielectric properties of low-temperature (400 °C) Hf0.5Zr0.5O2 films

Abstract

We report on the effect of the Hf0.5Zr0.5O2 (HZO) film thickness on the ferroelectric and dielectric properties using pulse write/read measurements. HZO films of thicknesses ranging from 5 to 20 nm were annealed at 400 °C for 1 min in a nitrogen ambient to be compatible with the back-end of the line thermal budget. As the HZO film thickness decreases, low-voltage operation (1.0 V or less) can be achieved without the dead layer effect, although switching polarization (Psw) tends to decrease due to the smaller grain size. Meanwhile, for 20-nm-thick HZO films prepared under the identical stress (similar TiN top electrode thickness and thermal budget), the Psw and dielectric constant are reduced because of additional monoclinic phase formation.