Thermal cyclic etching of silicon nitride using formation and desorption of ammonium fluorosilicate

Abstract

Abstract Novel selective cyclic etching of SiN over SiO 2 via the formation and desorption of ammonium fluorosilicate was developed. The formation of ammonium fluorosilicate was observed using X-ray photoelectron spectroscopy after hydrofluorocarbon-based radical exposure. Etching of SiN was observed after ammonium fluorosilicate was removed by thermal annealing. Cyclic etching tests were carried out by repeated radical exposure and thermal annealing. The etching depth increased on increasing the number of cycles. It was found that the cyclic etching is self-limiting because the etching depth does not depend on the radical exposure time but on the number of cycles.