Nitride-based light-emitting diodes with Ni/ITO p-type ohmic contacts

Abstract

The optical and electrical properties of Ni(5 nm)-Au(5 nm) and Ni(3.5 nm)-indium tin oxide (ITO) (60 nm) films were studied. It was found that the normalized transmittance of Ni/ITO film could reach 87% at 470 nm, which was much larger than that of the Ni-Au film. It was also found that the specific contact resistance was 5 /spl times/ 10/sup -4/ /spl Omega/ /spl middot/ cm/sup 2/ and 1 /spl times/ 10/sup -3/ /spl Omega/ /spl middot/ cm/sup 2/, respectively, for Ni-Au and Ni/ITO on p-GaN. Furthermore, it was found that the 20 mA output power of light-emitting diode (LED) with Ni-Au p-contact layer was 5.26 mW. In contrast, the output power could reach 6.59 mW for the LED with Ni/ITO p-contact layer.