Low On-Resistance High-Breakdown Normally Off AlN/GaN/AlGaN DHFET on Si Substrate

Abstract

Ultrathin-barrier normally off AlN/GaN/AlGaN double-heterostructure field-effect transistors using an in situ SiN cap layer have been fabricated on 100-mm Si substrates for the first time. The high 2DEG density in combination with an extremely thin barrier layer leads to enhancement-mode devices with state-of-the-art combination of specific on-resistance that is as low as 1.25 m¿·cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> and breakdown voltage of 580 V at <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">V</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">GS</sub> = 0 V . Despite the 2-¿m gate length used, the transconductance peaks above 300 mS/mm. Furthermore, pulsed measurements show that the devices are dispersion free up to high drain voltage <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">V</i> <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">DS</sub> = 50 V. More than 200 devices have been characterized in order to confirm the reproducibility of the results.