Temperature-dependent magnetoresistance of magnetic tunnel junctions with ultraviolet light-assisted oxidized barriers

Abstract

Co(10 nm)/AlO x ( nominally 2 nm)/Co(20 nm) tunnel junctions have been prepared under ultrahigh vacuum conditions applying a shadow mask technique. An ultraviolet light-assisted oxidation process of the AlOx barrier has been optimized by in situ x-ray photoelectron spectroscopy, in conjunction with temperature-dependent tunneling magnetoresistance measurements. Optimum-oxidized tunnel junctions show a magnetoresistance of 20% at 285 K, and up to 38% at 100 K. For under-oxidized samples, with a remaining Al layer between the Co bottom electrode and the AlOx barrier, the tunneling magnetoresistance decreases more rapidly with increasing temperature than observed for the over-oxidized samples. The resistance × area product of optimum-oxidized tunneling junctions exhibits a minimum, and increases for under- and over-oxidized samples.