Indium tin oxide/InGaZnO bilayer stacks for enhanced mobility and optical stability in amorphous oxide thin film transistors

Abstract

Optically more stable, high mobility InGaZnO thin film transistors were fabricated by implementing ultrathin In2O3-SnO2 (ITO) layers at the gate dielectric/semiconductor interface. The optimized device portrayed a high saturation mobility of ∼80 cm2/V s with off current values lower than 10−11A. The ITO layer also acted as a hole filter layer, and hole current and threshold voltage shift values measured under negative bias illumination conditions showed that a significant amount of photo-generated charge carriers were annihilated before reaching the gate insulator. This effect was more evident at larger intensities, showing threshold voltage shift values reduced by more than ∼70% under stress conditions.