Strontium doped hafnium oxide thin films: Wide process window for ferroelectric memories

Abstract

Ferroelectricity in hafnium oxide has been reported for the incorporation of Al, Si, Y and Gd or in a solid solution with the chemically similar ZrO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> . Here, we report strontium as the first bivalent and — so far — largest dopant in terms of atomic radius also inducing ferroelectric behavior. Besides the solid solution of HfO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /ZrO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> for Sr:HfO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> , ferroelectricity is observed in the widest concentration range of all dopants used up to now. First results of ab initio simulations also suggest such a comparatively wide window for ferroelectricity. With a coercive field of about 2 MV/cm another figure exceeds the characteristics reported before. A maximum remanent polarization of 23 μC/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> also ranks among the highest values reported until now. The fabricated TiN-Sr:HfO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> -TiN capacitors exhibit switching times in the nanosecond range and still retain 80 % of their initial remanent polarization after 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> endurance cycles. The 10 nm ferroelectric thin films prepared by atomic layer deposition are capable of integration into 3D capacitors or FinFETs.