Journal of the American Ceramic Society · 2014 · 14 citations · 40 references
Natural SciencesMaterials EngineeringMaterials ScienceElectronic MaterialsMaterials CharacterizationThin FilmsAmorphous MaterialsAmorphous SolidsDopingNanomaterial CharacterizationThin Film Electrical PropertiesThin-film MaterialsAmorphous Thin FilmsConductivityConductivity In Thin FilmsDoping In Thin FilmsNanocrystalline Thin FilmsNanocrystalsP-type ConductivityThin Oxide Films
This article reports the characterization of thin films sputtered from CuAl 1− x Ca x O targets ( x = 0, 0.05, 0.1, 0.15, and 0.2) at room temperature. All films exhibit amorphous/nanocrystalline structures. Their transparency increases slightly with the addition of Ca . Furthermore, the resistivity decreases as the Ca / Al atomic ratio increases. Transmission electron microscopy with energy dispersive spectroscopy mapping indicates that the composition is uniform throughout the films deposited from the highest Ca doping concentration target. Some nanocrystals are present at the top surface of the CuAl 0.8 Ca 0.2 O thin film as well as the interface region between the CuAl 0.8 Ca 0.2 O thin film and the glass substrate, whereas the interior of the film is pretty amorphous with some embedded nanocrystals. X‐ray photoelectron spectroscopy shows that the Cu 2+ / Cu + atomic ratio increases with the Ca / Al atomic ratio, indicating the enhancement of p ‐type conductivity from the nonisovalent Cu – O alloying.
40
P-type electrical conduction in transparent thin films of CuAlO2
Hiroshi Kawazoe, Masahiro Yasukawa, Hiroyuki Hyodo et al. · Nature · 1997 · 2.1K citations
Natural Sciences, Materials Engineering, Materials Science +14
Complementary Metal Oxide Semiconductor Technology With and On Paper
Rodrigo Martins, Arokia Nathan, Raquel Barros et al. · Advanced Materials · 2011 · 253 citations