Ion Irradiation-Induced Interface Mixing and the Charge Trap Profiles Investigated by In Situ Electrical Measurements in Pt/Al₂O₃/ β-Ga₂O₃ MOSCAPs

Abstract

In situ <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${I} - {V}$ </tex-math></inline-formula> and <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${C}\!\!-\!\!{V}$ </tex-math></inline-formula> measurements were performed during the 120 MeV Au <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{9+}$ </tex-math></inline-formula> ion irradiation on the Pt/Al <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$_{{2}}\text{O}_{{3}}/\beta $ </tex-math></inline-formula> -Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> , metal–oxide–semiconductor capacitors (MOSCAPs), to comprehend the swift heavy ion (SHI)-induced effects at the interface and in the device performance. At a maximum fluence of <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$2\times 10^{{12}}$ </tex-math></inline-formula> ions/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> , the <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${I}-\!{V}$ </tex-math></inline-formula> data showed a rise in the reverse leakage current by four orders of magnitude compared to the pristine device. The trap level (below the conduction band of Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3)</sub> from Poole–Frenkel emission exhibits a variation from <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\sim $ </tex-math></inline-formula> 1.1 to 0.91 eV. The conduction band offset <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${(\phi }_{B}{) }$ </tex-math></inline-formula> of Al <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$_{{2}}\text{O}_{{3}}/\beta $ </tex-math></inline-formula> -Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> changes from 1.48 to 1.25 eV as estimated under the Fowler–Nordheim tunneling mechanism. In situ <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">${C}\!\!-\!\!{V}$ </tex-math></inline-formula> measurements show a significant shift in the flat band voltages and increased oxide in the border and interface due to charge trapping. The X-ray photoelectron spectroscopy (XPS) measurements of Al 2p and O 1s core levels revealed the pre-existing oxygen defects in Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> , which increase with fluence. The deconvoluted peaks of Al 2p at 74.6 eV designated to Al-sub oxide and the O 1s peak variation in the FWHM signifies the increase in the O defects. Cross-sectional transmission electron microscopy (XTEM) measurements on the irradiated device (at <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$2\times 10^{{12}}$ </tex-math></inline-formula> ions/cm <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{{2}}{)}$ </tex-math></inline-formula> revealed a modulated interface of Al <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$_{{2}}\text{O}_{{3}}/\beta $ </tex-math></inline-formula> -Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> and the formation of an interlayer of <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\sim $ </tex-math></inline-formula> 4 nm Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"><i>x</i></sub> Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">y</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">z</sub> . The scanning transmission electron microscope (STEM)-based high-angle annular dark-field imaging (HAADF) energy-dispersive X-ray spectroscopy (EDS) mapping revelation and the depth profiles of XPS data confirm the formation of an Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"><i>x</i></sub> Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">y</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">z</sub> interlayer.