Mechanical and antimicrobial properties of low‐density‐polyethylene/<scp>MgO</scp> nanocomposites

Abstract

Abstract Low‐density polyethylene (LDPE) nanocomposites containing magnesium oxide (MgO) nanoparticles are obtained by melt mixing. MgO nanoparticles ca. 29 ± 2 nm are synthesized by sol–gel and organically modified on the surface with oleic acid (Mod‐MgO), whose final concentration in the polymers is 3, 5, and 10 wt%. The presence of these nanoparticles did not affect the crystallization process of LDPE. However, Young's modulus increases with 10 wt% of Mod‐MgO nanoparticles, rendering higher reinforcement effects with an increase as high as 48%. This affects the elongation at break, which decreases ca. 57% compared to neat LDPE. The storage and loss modulus of the LDPE/MgO and LDPE/Mod‐MgO nanocomposites increases at room temperature and low temperatures (−150 to −50°C) compared to neat LDPE. SEM analysis showed that the organic modification of MgO nanoparticles improved their dispersion within the polymer matrix. Nanocomposites present antimicrobial properties against Escherichia coli , reaching an efficiency ca. 53%.