Single pulse femtosecond laser ablation of silicon – a comparison between experimental and simulated two-dimensional ablation profiles

Abstract

Abstract Ultrashort laser pulses are widely used for the precise structuring of semiconductors like silicon (Si). We present here, for the first time, a comparative study of experimentally obtained and numerically simulated two-dimensional ablation profiles based on parameters of commercially relevant and widely used near-infrared and diode pumped femtosecond lasers. Single pulse laser ablation was studied at a center wavelength of 1040 nm and pulse duration of 380 fs (FWHM) in an irradiating fluence regime from 1 J/cm 2 to 10 J/cm 2 . Process thresholds for material transport and removal were determined. Three regimes, scaling with the fluence, could be identified: low and middle fluence regimes and a hydrodynamic motion regime. By comparing the simulated and experimental ablation profiles, two conclusions can be drawn: At 2 J/cm 2 , the isothermal profile of 3800 K is in excellent agreement with the observed two-dimensional ablation. Thus exceeding a temperature of 3800 K can be accepted as a simplified ablation condition at that fluence. Furthermore, we observed a distinct deviation of the experimental from the simulated ablation profiles for irradiated fluences above 4 J/cm 2 . This points to hydrodynamic motion as an important contributing mechanism for laser ablation at higher fluences.