Size-Dependent Bandwidth of Semipolar ( $11\overline {2}2$ ) Light-Emitting-Diodes

Abstract

The limited modulation bandwidth of commercial light-emitting diodes (LEDs) is one of the critical bottlenecks for visible light communications. Possible approaches to increase the bandwidth include the use of micron sized LEDs, which can withstand higher current densities, as well as the use of LED structures that are grown on different crystal planes to the conventional polar c-plane. We compare c-plane InGaN/GaN LEDs with semipolar (112̅2) LEDs containing a 4- and 8-nm single quantum well. The modulation bandwidth of semipolar LEDs with active areas varying from 200 × 200 to 30 × 30 μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> is shown to be governed by both current density and size. A small signal bandwidth of over 800 MHz for a relatively low applied current density of 385 A/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> is reported for 30 × 30 μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> LEDs with 8-nm thick quantum well. An optical link using an easy non-return-to-zero ON-OFF keying modulation scheme with a data rate of 1.5 Gb/s is demonstrated.