High transconductance InGaAs/AlGaAs pseudomorphic modulation-doped field-effect transistors

Abstract

Pseudomorphic In <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.15</inf> Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.85</inf> As/Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.15</inf> Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.85</inf> As modulation-doped field effect transistors (MODFET's) exhibiting extremely good dc characteristics have been successfully fabricated, dc transconductance in these strained-layer structures of 270 mS/mm were measured for 1-µm gate, normally-on devices at 300 K. Maximum drain current levels are 290 mA/mm, with excellent pinch-off and saturation characteristics. The transconductance increased to 360 mS/mm at 77 K while no persistent photoconductivity or drain collapse was observed. Preliminary microwave results indicate a 300-K current gain cutoff frequency of about 20 GHz. These results are equivalent to the best GaAs/AlGaAs MODFET results and are due in part to the improved transport properties and carrier confinement in the InGaAs quantum well.