High-mobility thin-film transistor with amorphous InGaZnO4 channel fabricated by room temperature rf-magnetron sputtering

Abstract

Thin-film transistors (TFTs) were fabricated using amorphous indium gallium zinc oxide (a-IGZO) channels by rf-magnetron sputtering at room temperature. The conductivity of the a-IGZO films was controlled from ∼10−3to10−6Scm−1 by varying the mixing ratio of sputtering gases, O2∕(O2+Ar), from ∼3.1% to 3.7%. The top-gate-type TFTs operated in n-type enhancement mode with a field-effect mobility of 12cm2V−1s−1, an on-off current ratio of ∼108, and a subthreshold gate voltage swing of 0.2Vdecade−1. It is demonstrated that a-IGZO is an appropriate semiconductor material to produce high-mobility TFTs at low temperatures applicable to flexible substrates by a production-compatible means.