Novel symmetry in the growth of gallium nitride on magnesium aluminate substrates

Abstract

The growth of GaN by metalorganic chemical vapor deposition on (111) and (100) magnesium aluminate (MgAl2O4) substrates is examined using transmission electron microscopy. The results indicate that mainly wurtzite GaN is grown for both orientations. On the (111) substrate the following epitaxial relationship is observed: (0001)GaN ∥ (111)MgAl2O4, and [112̄0]GaN ∥ [11̄0]MgAl2O4. During the early stages of the (100) growth, four orientations of the wurtzite phase and a zinc-blende phase are formed. With increasing thickness, one of the wurtzite orientations dominates, with the epitaxial relationship being (11̄01)GaN ∥ (100)MgAl2O4 and the [112̄0]GaN nearly parallel to [011]MgAl2O4. This choice of growth orientation appears to be determined primarily by the nature of the interfacial bonding, with the basal plane of each of the four wurtzite GaN variants being nearly aligned along one of the four {111} planes intersecting the (100) surface of the MgAl2O4.