Seal Formation in Silicon Planar Patch-Clamp Microstructures

Abstract

This paper presents a microfabricated planar patch-clamp electrode design and looks at the impact of several physical characteristics on seal formation. The device consists of a patch aperture, 1.5-2.5 mum in diameter and 7-12 mum in depth, with a reverse-side deep-etched 80-mum well. The patch aperture was coated with either thermal oxide or plasma-enhanced chemical vapor deposited (PECVD) SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> . Some of the thermal oxide devices were converted into protruding nozzle structures, and some were boron-doped. Seal formation was tested with cultured N2a neuroblastoma cells. The PECVD oxide devices produced an average seal resistance of 34 MOmega(n = 24), and the thermal oxide devices produced an average seal resistance of 96 MOmega(n = 59). Seal resistance was found to positively correlate with patch aperture depth. Whole-cell recordings were obtained from 14% of cells tested with the thermal oxide devices, including a single recording where a gigaohm seal was obtained.