Direct observation of Cu, Zn cation disorder in Cu₂ZnSnS₄ solar cell absorber material using aberration corrected scanning transmission electron microscopy

Abstract

ABSTRACT Chemical analysis of individual atom columns was carried out to determine the crystal structure and local point defect chemistry of Cu 2 ZnSnS 4 . Direct evidence for a nanoscale composition inhomogeneity, in the form of Zn enrichment and Cu depletion, was obtained. The lateral size of the composition inhomogeneity was estimated to be between ~1.5 and 5 nm. Photoluminescence confirmed the presence of a broad donor–acceptor transition consistent with the observed cation disorder. Areas of relatively high concentration of Zn Cu + antisite atom donors locally increases the electrostatic potential and gives rise to band bending. Troughs in the conduction band and peaks in the valence band are ‘potential wells’ for electrons and holes, respectively. For a solar cell, these prevent minority carrier electrons from diffusing towards the edge of the space charge region, thereby reducing the carrier separation efficiency as well as reducing the carrier collection efficiency of majority carrier holes. Furthermore, electrons and holes ‘trapped’ within potential wells in close proximity have a high probability of recombining, so that the carrier lifetime is also reduced. High quality Cu 2 ZnSnS 4 crystals free from composition inhomogeneities are therefore required for achieving high efficiency solar cell devices. Copyright © 2012 John Wiley & Sons, Ltd.