Titanium Silicide (TiSi ₂ is a primary contact material with low-resistance contact characteristics used in nanodevices. However, the rapid scaling trend requires further improvement to achieve both high thermal stability and low contact resistivity. Herein, a method for simultaneously improving the contact resistivity and thermal stability of the TiSi ₂ /Si interface is proposed by inserting a Ta interlayer into Ti/p-Si. The Ta-interlayered TiSi ₂ (Ta IL TiSi ₂ ) achieves an improved contact resistivity by approximately 7.9 times compared to that without the Ta interlayer. This remarkable improvement is due to the smooth contact morphology resulting from the suppressed excess diffusion of Ti and Si and dopant segregation at the TiSi ₂ /Si interface. Particularly, because additional reaction during post annealing is minimized by the Ta interlayer, Ta IL TiSi ₂ shows a low sheet resistance of

$3.71~\Omega /\Box $

even after post annealing at 600 °C & 30 min, which is much lower than the conventional TiSi ₂ scheme under the same annealing conditions. These results are expected to provide insights into state-of-the-art CMOS-based devices that require both low contact resistivity and better thermal margins.

	Year	Citations

About