Fluorescence Upconversion Properties of Er³⁺-Doped TiO₂ and BaTiO₃ Nanocrystallites

Abstract

The effects of the erbium concentration, crystal size, crystal phase, and different processing temperatures on the upconverted emission of Er 3+ in BaTiO 3 and TiO 2 nanocrystals are reported. A cw diode laser at 975 nm was used as a pump source for resonant sequential excitation of the 4 I 11/2 and 4 F 7/2 levels. Green and red upconversion emission at 550 and 670 nm were observed from these oxide nanocrystals with 975 nm excitation. With the same Er 3+ concentration, the upconversion emission intensity from BaTiO 3 was higher than that observed in the TiO 2 host. In the TiO 2 matrix, the maximum upconversion emission intensity of Er 3+ was found for samples calcined at 800 °C where both the anatase and the rutile phases were present. The observed emission characteristics and the pump intensity dependence of the luminescence intensity confirm that the upconverted emission in these materials is produced by two-photon excited-state absorption (ESA) processes.