Thermal stability and phase transformation of α-, κ(ε)-, and γ-Ga2O3 films under different ambient conditions

Abstract

Phase transitions in metastable α-, κ(ε)-, and γ-Ga2O3 films to thermodynamically stable β-Ga2O3 during annealing in air, N2, and vacuum have been systematically investigated via in situ high-temperature x-ray diffraction (HT-XRD) and scanning electron microscopy (SEM). These respective polymorphs exhibited thermal stability to ∼471–525 °C, ∼773–825 °C, and ∼490–575 °C before transforming into β-Ga2O3, across all tested ambient conditions. Particular crystallographic orientation relationships were observed before and after the phase transitions, i.e., (0001) α-Ga2O3 → (2¯01) β-Ga2O3, (001) κ(ε)-Ga2O3 → (310) and (2¯01) β-Ga2O3, and (100) γ-Ga2O3 → (100) β-Ga2O3. The phase transition of α-Ga2O3 to β-Ga2O3 resulted in catastrophic damage to the film and upheaval of the surface. The respective primary and possibly secondary causes of this damage are the +8.6% volume expansion and the dual displacive and reconstructive transformations that occur during this transition. The κ(ε)- and γ-Ga2O3 films converted to β-Ga2O3 via singular reconstructive transformations with small changes in volume and unchanged surface microstructures.