Rational Design of Zincophilic Ag/Permselective PEDOT:PSS Heterogeneous Interfaces for High‐Rate Zinc Electrodeposition

Abstract

Abstract Designing artificial interface is a promising strategy to protect Zn metal anode but achieving long Zn plating/stripping lifespans and efficient nucleation/deposition kinetics, particularly at high current densities, remains a challenge. In this study, a permselective zincophilic heterogeneous interface consisting of metallic Ag layer and poly(3,4‐ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) is designed via a simple chemical displacement and drop casting process. The artificial interface plays a multifunctional role in inhibiting dendrite growth/side reactions by reducing the nucleation barrier through a large number of Zn nucleation sites offered by the bottom Ag layer, homogenizing electrical field/Zn 2+ flux and shielding SO 4 2− migration via the compact, conducting, and Zn 2+ ‐permselective PEDOT:PSS supporting layer. Moreover, the heterogeneous interface demonstrates enhanced structural integrity owing to the binder effect of PEDOT:PSS. As a result, the modified Zn anode demonstrates a cyclic lifespan of 200 h and a reduced voltage hysteresis of ≈150 mV at 20 mA cm −2 /5 mAh cm −2 , far surpassing its counterparts. Moreover, the protected Zn anode allows the LiMn 2 O 4 ‐based full cells with remarkable rate and cycling performance. These findings provide new insight into the design of an efficient artificial interface for highly reversible and high‐rate Zn electrodeposition.