Electrically driven, polarized, phosphor-free white semipolar (20-21) InGaN light-emitting diodes grown on semipolar bulk GaN substrate

Abstract

We demonstrate a simple method to fabricate efficient, electrically driven, polarized, and phosphor-free white semipolar (20-21) InGaN light-emitting diodes (LEDs) by adopting a top blue quantum well (QW) and a bottom yellow QW directly grown on (20-21) semipolar bulk GaN substrate. At an injection current of 20 mA, the fabricated 0.1 mm 2 size regular LEDs show an output power of 0.9 mW tested on wafer without any backside roughing, a forward voltage of 3.1 V and two emission peaks located at 427 and 560 nm. A high polarization ratio of 0.40 was measured in the semipolar monolithic white LEDs, making them promising candidates for backlighting sources in liquid crystal displays (LCDs). Furthermore, a 3dB modulation bandwidth of 410 MHz in visible light communication (VLC) was obtained in the micro-size LEDs (µLEDs) with a size of 20×20 µm 2 and 40×40 µm 2 , which could overcome the limitation of slow frequency response of yellow phosphor in commercial white LEDs combing blue LEDs and yellow phosphor.