Enhanced Performance of Atomic Layer Deposited Thin-Film Transistors With High-Quality ZnO/Al₂O₃ Interface

Abstract

We fabricated ZnO channel/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> gate dielectric thin-film transistors (TFTs) by atomic layer deposition (ALD) continuous growth process. The effects of the channel and the dielectric continuous growth on the performance of TFTs were investigated. Compared with noncontinuous growth ZnO/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films, continuous growth ZnO/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films with no obvious buffer layer and less residual O-H bonds possess superior ZnO/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> interface quality. The continuous growth TFTs exhibit a field-effect mobility of 19.6 cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> V <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> s <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> , a subthreshold swing of 0.13 V dec <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> , a high ION/IOFF of 4.1 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">9</sup> , a hysteresis window of 0.09 V, and an excellent uniformity of electrical characteristics. Continuous growth TFTs also demonstrate better stability with minor shifts of ΔV <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">th</sub> 0.6 V [positive bias stress (PBS)] and ΔV <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">th</sub> - 0.3 V [negative bias stress (NBS)]. The faster falling rates of activation energy for continuous growth TFTs indicate that the total trap density is reduced through the continuous growth of active layer and dielectric layer. Our results suggest that the ALD-based continuous growth process could enhance the performance of TFTs.