Highly Sensitive, Fast Response Perovskite Photodetectors Demonstrated in Weak Light Detection Circuit and Visible Light Communication System

Abstract

Abstract Organic–inorganic hybrid perovskite (OIHP) photodetectors have presented unprecedented device performance mainly owing to outstanding material properties. However, the solution‐processed OIHP polycrystalline thin films with defective surface and grain boundaries always impair the key parameter of photodetectors. Herein, a nonfullerene passivation layer exhibits more efficient passivation for OIHP materials to dramatically reduce the trap density of state, yielding a dark current as low as 2.6 × 10 −8 A cm −2 under −0.1 V. In addition, the strong absorption in near‐infrared (NIR) region of nonfullerene/C 60 heterojunction broadens the detectable range to over 900 nm by effective charge transport, ultimately leading to a specific detectivity of 1.45 × 10 12 and 7.37 × 10 11 cm Hz 1/2 W −1 at 650 and 820 nm, respectively. Encouragingly, the response speed of 27 ns is obtained at 0.6 mm 2 of device area by removing constrain from the resistance–capacitance constant. Moreover, the prominent practical application of the photodetector is demonstrated in a weak light detection circuit and a visible light communication system. It is believed that the OIHP photodetectors with high sensitivity, NIR photoresponse, and ultrafast speed would pave the way to commercial applications.