Direct van der Waals Epitaxy of Crack-Free AlN Thin Film on Epitaxial WS2

Abstract

Van der Waals epitaxy (vdWE) has drawn continuous attention, as it is unlimited by lattice-mismatch between epitaxial layers and substrates. Previous reports on the vdWE of III-nitride thin film were mainly based on two-dimensional (2D) materials by plasma pretreatment or pre-doping of other hexagonal materials. However, it is still a huge challenge for single-crystalline thin film on 2D materials without any other extra treatment or interlayer. Here, we grew high-quality single-crystalline AlN thin film on sapphire substrate with an intrinsic WS₂ overlayer (WS₂/sapphire) by metal-organic chemical vapor deposition, which had surface roughness and defect density similar to that grown on conventional sapphire substrates. Moreover, an AlGaN-based deep ultraviolet light emitting diode structure on WS₂/sapphire was demonstrated. The electroluminescence (EL) performance exhibited strong emissions with a single peak at 283 nm. The wavelength of the single peak only showed a faint peak-position shift with increasing current to 80 mA, which further indicated the high quality and low stress of the AlN thin film. This work provides a promising solution for further deep-ultraviolet (DUV) light emitting electrodes (LEDs) development on 2D materials, as well as other unconventional substrates.