Inverted Planar Perovskite Solar Cells with a High Fill Factor and Negligible Hysteresis by the Dual Effect of NaCl-Doped PEDOT:PSS

Abstract

The performance of inverted perovskite solar cells is highly dependent on hole extraction and surface properties of hole transport layers. To highlight the important role of hole transport layers, a facile and simple method is developed by adding sodium chloride (NaCl) into poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). The average power conversion efficiency of the perovskite solar cells prepared on NaCl-doped PEDOT:PSS is 17.1% with negligible hysteresis, compared favorably to the control devices (15.1%). Particularly, they exhibit markedly improved V oc and fill factor (FF), with the best FF as high as 81.9%. The enhancement of photovoltaic performance is ascribed to two effects. Better conductivity and hole extraction of PEDOT:PSS are observed after NaCl doping. More intriguingly, the perovskite polycrystalline film shows a preferred orientation along the (001) direction on NaCl-doped PEDOT:PSS, leading to a more uniform thin film. The comparison of the crystal structure between NaCl and MAPbCl 3 indicates a lattice constant mismatch less than 2% and a matched chlorine atom arrangement on the (001) surface, which implies that the NaCl crystallites on the top surface of PEDOT:PSS might serve as seeds guiding the growth of perovskite crystals. This simple method is fully compatible with printing technologies to mass-produce perovskite solar cells with high efficiency and tunable crystal orientations.