Bond strength of a self-etching adhesive system to caries-affected dentin.

Abstract

This in vitro study evaluated the microtensile bond strengths of sound versus caries-affected dentin using a self-etching adhesive system, Clearfil SE Bond, with or without additional acid pre-conditioning. Extracted human mandibular molars with occlusal caries extending halfway through the dentin were used. In the first group, the teeth were bonded with the self-etching adhesive Clearfil SE Bond according to the manufacturer's instructions. In the second group, prepared dentin surfaces were etched with 37% phosphoric acid prior to applying the same self-etching adhesive. After the bonding procedure, all specimens were built up with composite resin and stored in water for 24 hours. The teeth were serially sectioned vertically into 0.7-mm slabs and trimmed into an hourglass shape for measuring microtensile bond strength. Each specimen was attached to a Bencor device and stressed in tension at a crosshead speed of 1 mm/minute. Statistical analysis was performed using two-way ANOVA and the Tukey HSD test (p<0.05). The microtensile bond strengths of Clearfil SE Bond to sound dentin (32.9) were significantly higher than to caries-affected dentin (15.9). In the second group where acid etching was performed prior to applying Clearfil SE Bond, there were no statistically significant differences between the microtensile bond strengths of sound (19.2) and caries-affected dentin (16.3). While bond strengths to sound dentin were decreased by using additional acid etching prior to applying Clearfil SE Bond, this procedure revealed no statistically significant differences in bond strengths for the caries-affected dentin.