A rheological and morphological study of a copolyester liquid crystal/polypropylene blend system

Abstract

The effects of composition and shear rate on the rheology and morphology of blends of LC–3000, a thermotropic liquid crystalline polymer consisting of 60/40 of hydroxybenzoic acid and poly(ethylene terephthalate), with polypropylene were studied. It was found that the rheological properties depend in a complex manner on composition and applied shear. Both positive and negative deviations from the log-additivity rule were observed at low shear rates. Significant viscosity reduction was measured when the dispersed phase was a nematic TLCP. The accompanying microstructural transitions were characterized a posteriori, and it was found that the state of dispersion of the TLCP phase also influences the viscosity reduction phenomenon. A nematic, fibrillar TLCP phase shows a viscosity reduction of the order of fourfold with respect to the viscosity of the matrix. Another important finding was that the stability of these fibers would not be expected from work on other non-TLCP-containing immiscible blends. This suggests that the unique rheology of the TLCP minor phase is relevant to the formation of stable fibers. © 1996 John Wiley & Sons, Inc.