Protection of Fe pigments with amine-quinone polymers

Abstract

High magnetization iron pigments, protected by amine-quinone polymers are described. The amine-quinone polyurethanes were prepared by melt polymerization of 2,5-bis(N-2-hydroxyethyl-N-methylamino)-1,4-benzoquinone, AQM-1, tolylene diisocyanate, and an oligomeric polyether diol; either poly(1,2-butylene glycol) or poly(1,4-butylene glycol). Depending on the choice of polyether and the relative amount of AQM-1, the polyurethanes were elastomeric or thermoplastic; the thermal and mechanical properties being systematically controlled by the polymer structure. Hydrogen reduction of acicular iron oxide pigments gave pyrophoric Fe pigments with an initial /spl sigma//sub s//spl ap/195 emu/g. Treatment with a THF solution of the amine-quinone polymer AQPU-8, under an inert atmosphere, gave stabilized Fe pigments with /spl sigma//sub s//spl ap/160 to 180 emu/g; a value significantly higher than 140 emu/g for the best ceramic coated pigments. The treated pigments were exposed to the ambient laboratory atmosphere for more than 3000 hours with no loss in /spl sigma//sub s/. This demonstration that quinone polymers can replace the ceramic coatings used to protect iron pigments provides a means of significantly enhancing the performance of metal particle tape.< <ETX xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">&gt;</ETX>