Mobility Enhancement and OFF Current Suppression in Atomic-Layer-Deposited ZnO Thin-Film Transistors by Post Annealing in O₂

Abstract

The impacts of postdeposition annealing in O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> on the electrical performance of atomic-layer-deposited ZnO thin-film transistors (TFTs) have been investigated. The TFTs are fabricated on transparent quartz substrates with Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> dielectrics, ZnO active layers, and Cr/Au electrodes. The best field-effect mobility of 21.3 cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> /Vs and a large ON/OFF current ratio of 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7</sup> are obtained under 400°C annealing treatment in O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> . Furthermore, analysis indicates that reduction of OH bonds in both ZnO and Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> layers is the key issue to achieve the excellent properties.