A $\hbox{TiO}_{2}$ Nanowire MIS Photodetector With Polymer Insulator

Abstract

The authors report the growth of TiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> nanowires by heating the Ti/glass template and the fabrication of a TiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> nanowire metal-insulator-semiconductor (MIS) photodetector (PD). Compared with a TiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> nanowire metal-semiconductor- metal PD, it was found that we could achieve a photocurrent 29 times larger. It was also found that the dynamic response of the TiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> nanowire MIS PD was stable and reproducible with an on/off current contrast ratio of around 180. With an incident light wavelength of 390 nm and an applied bias of 5 V, it was found that the measured responsivity of the PD was 2.46 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-3</sup> A/W. Furthermore, the noise equivalent power and the detectivity of the fabricated TiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> nanowire MIS PD were 7.49 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-12</sup> W and 8.86 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">11</sup> cm · Hz <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.5</sup> · W <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> , respectively.