SYNTHESIS, CHARACTERIZATION AND SINGLE-BEAM Z-SCAN MEASUREMENT OF THE THIRD-ORDER OPTICAL NONLINEARITIES OF <font>ZnO</font> NANO-PARTICLES

Abstract

Nano-particle materials with large optical nonlinearities are in great need for the development of nonlinear optical technology and are being studied intensively in recent years. ZnO nanoparticles have been synthesized by precipitation from zinc acetate in a series of n-alkanols from ethanol to 1-hexanol as a function of temperature. The formation and microstructure of ZnO particles were monitored by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-Vis spectrum and z-scan technique. We studied the optical limiting effect of ZnO nano-particles. Using a CW He - Ne laser at 632.8 nm. The UV-Visible spectrum of this material shows a 373.5 nm peak. Using the UV-Visible, the band gap of this nano-particle is obtained about 3.31 eV. Also the XRD spectroscopy indicates that the structure is wurtzite hexagonal. Average particle size obtained from SEM analysis about 43nm. Furthermore the nonlinear refractive index, n 2 , and nonlinear absorption coefficient, β, were measured using close and open aperture z-scan respectively, at peak laser irradiation of 1.743 kW/cm 2 . Then the nonlinear refraction index of this nano-particle was measured in order of 10 -7 (cm 2 /W) with negative sign and the nonlinear absorption coefficient was obtained in order of 10 -3 (cm/W).