Anisotropic electrical conduction from heterogeneous oxidation states in plasma sprayed TiO2 coatings

Abstract

Microstructural and electrical characterizations of air plasma sprayed TiO2 coatings were carried out to investigate the details of deoxidation during the spray process and the changes following air annealing. The coatings were found to behave as an n-type semiconductor indicating the presence of oxygen vacancies. Direct-current resistivity measurements in plane (ρIP) and through thickness (ρTT) of the coatings as a function of annealing time and temperature showed remarkably large anisotropies (=ρTT∕ρIP) of up to 105. Impedance spectroscopy of the specimens coupled with microstructural analysis revealed that the origin of this anisotropy lies in the heterogeneous deoxidation and reoxidation behavior of the coatings. Due to rapid quenching, the high temperature deoxidation state is preserved in the splat boundaries making them more conductive than the bulk of the splat in the as-sprayed coating. Upon annealing in air, the splat boundaries get selectively oxidized due to faster surface diffusion of oxygen and become more insulating. This behavior, together with the layered morphology of plasma sprayed coatings, results in anisotropy.