Excess Avalanche Noise in $\hbox{In}_{0.52}\hbox{Al}_{0.48}\hbox{As}$

Abstract

Avalanche multiplication and excess noise arising from both electron and hole injection have been measured on a series of In <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.52</sub> Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.48</sub> As p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> -i-n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> and n <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> -i-p <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">+</sup> diodes with nominal avalanche region widths between 0.1 and 2.5 mum. With pure electron injection, low excess noise was measured at values corresponding to effective k=beta/alpha between 0.15 and 0.25 for all widths. Enabled ionization coefficients were deduced using a non-local ionization model utilizing recurrence equation techniques covering an electric field range from approximately 200 kV/cm to 1 MV/cm