1e:T556,Quasi-2D perovskites have long been considered to have favorable "energy funnel/cascade" structures and excellent optical properties compared with their 3D counterparts. However, most quasi-2D perovskite light-emitting diodes (PeLEDs) exhibit high external quantum efficiency (EQE) but unsatisfactory operating stability due to Auger recombination induced by high current density. Herein, a synergetic dual-additive strategy is adopted to prepare perovskite films with low defect density and high environmental stability by using 18-crown-6 and poly(ethylene glycol) methyl ether acrylate (MPEG-MAA) as the additives. The dual additives containing COC bonds can not only effectively reduce the perovskite defects but also destroy the self-aggregation of organic ligands, inducing the formation of perovskite nanocrystals with quasi-core/shell structure. After thermal annealing, the MPEG-MAA with its CC bond can be polymerized to obtain a comb-like polymer, further protecting the passivated perovskite nanocrystals against water and oxygen. Finally, state-of-the-art green PeLEDs with a normal EQE of 25.2% and a maximum EQE of 28.1% are achieved, and the operating lifetime (T₅₀ ) of the device in air environment is over ten times increased, providing a novel and effective strategy to make high efficiency and long operating lifetime PeLEDs.1f:T47f,Tin-based perovskites with excellent optoelectronic properties and suitable band gaps are promising candidates for the preparation of efficient lead-free perovskite solar cells (PSCs). However, it is challenging to prepare highly stable and efficient tin-based PSCs because Sn²⁺ in perovskites can be easily oxidized to Sn⁴⁺ upon air exposure. Here we report the fabrication of air-stable FASnI₃ solar cells by introducing hydroxybenzene sulfonic acid or its salt as an antioxidant additive into the perovskite precursor solution along with excess SnCl₂ . The interaction between the sulfonate group and the Sn²⁺ ion enables the in situ encapsulation of the perovskite grains with a SnCl₂ -additive complex layer, which results in greatly enhanced oxidation stability of the perovskite film. The corresponding PSCs are able to maintain 80 % of the efficiency over 500 h upon air exposure without encapsulation, which is over ten times longer than the best result reported previously. Our results suggest a possible strategy for the future design of efficient and stable tin-based PSCs.

	Year	Citations

References