Impact of Dual Functionalities of Mo‐Doped BiFeO₃ Decorated with Bi₄MoO₉ Heteroatoms for Piezo‐Photocatalytic Activity

Abstract

Abstract Piezocatalysts have shown great promise for effcient hydrogen generation. However, their application is limited by the rapid charge recombination and sluggish charge transfer rate of piezo‐induced charge carriers. This work aims to address the preceding limitations by controlled synthesis of a representative piezocatalyst, BiFeO 3 doped with Mo atoms and decorated with Bi 4 MoO 9 (BMO) heteroatoms using sol‐gel method. The substitutional doping of Mo on BFO (BFMO) was shown to induce a shallow energy level near the conduction band that acted as a trapping state, to suppress recombination of charge carriers, enhance charge mobility for transport to the surface, modulate band alignment, and lower the energy barrier for surface reaction. The formation of BFMO/BMO heterostructures induced electrical band bending, leading to the electric potential gradient, hence promoting charge carrier separation and transfer. The BFMO/BMO with 0.5 mol % Mo (Mo‐5) demonstrated four times faster piezocatalytic Rhodamine B (RhB) dye degradation rate ( k of 0.032 min −1 ) compared to pristine BFO (0.009 min −1 ). Further, the Mo‐5 exhibited a 45% higher piezocatalytic H 2 production rate (14.4 µmol/g/h) compared to pristine BFO (9.8 µmol/g/h) while being cocatalyst‐free. Coupling piezocatalysis with photocatalysis was found to reduceperformance relative to the individual processes, which is attributed to Auger recombination which impedes any potential synergistic effect.