Ultrathin Boundary-Less SnO₂ Films with Surface-Activated Two-Dimensional Nanograins Enable Fast and Sensitive Hydrogen Gas Sensing

Abstract

Fast and reliable semiconductor hydrogen sensors are crucially important for the large-scale utilization of hydrogen energy. One major challenge that hinders their practical application is the elevated temperature required, arising from undesirable surface passivation and grain-boundary-dominated electron transportation in the conventional nanocrystalline sensing layers. To address this long-standing issue, in the present work, we report a class of highly reactive and boundary-less ultrathin SnO 2 films, which are fabricated by the topochemical transformation of 2D SnO transferred from liquid Sn–Bi droplets. The ultrathin SnO 2 films are purposely made to consist of well-crystallized quasi-2D nanograins with in-plane grain sizes going beyond 30 nm, whereby the hydroxyl adsorption and grain boundary side-effects are effectively suppressed, giving rise to an activated (101)-dominating dangling-bond surface and a surface-controlled electrical transportation with an exceptional electron mobility of 209 cm 2 V –1 s –1 . Our work provides a new cost-effective strategy to disruptively improve the gas reception and transduction of SnO 2 . The proposed chemiresistive sensors exhibit fast, sensitive, and selective hydrogen sensing performance at a much-reduced working temperature of 60 °C. The remarkable sensing performance as well as the simple and scalable fabrication process of the ultrathin SnO 2 films render the thus-developed sensors attractive for long awaited practical applications in hydrogen-related industries.