1e:T4ec,Abstract The reduced graphene oxide (rGO) sponges exhibit exciting electromagnetic absorption (MA) performance in high‐frequency range. However, it is still a great challenge to realize desirable MA property at low frequency (2–4 GHz) due to the great difficulty in balancing the good interfacial impedance matching and strong dielectric loss. Herein, the MA metamaterials based on rGO sponge with different unit shapes are reported. The relationship between the unit shape and MA performance is explored by experiment and simulation. The results show that frustum pyramid metamaterial exhibits ultrabroad band MA; the qualified absorption (the reflection loss lower than −10 dB) of electromagnetic wave can be achieved at 2.4–40 GHz. The average absorption intensity is −22.9 dB in the band of 2–40 GHz. Moreover, the bandwidth for strong absorption with an absorption rate of 99% (−20 dB) is up to 32 GHz. It is significant that the reflection loss has ignorant change even though the incident angle is increased from 5° to 40°. These are contributed to the excellent impedance matching and strong dielectric loss. These lightweight frustum pyramid metamaterials are very promising in the application for broadband electromagnetic protection.1f:T4e0,Lightweight structures with multi-functions such as electromagnetic wave absorption and excellent mechanical properties are required in spacecraft. A three-dimensional metamaterial absorber consisting of honeycomb and resistive films was proposed and fabricated through 3D printing and silk-screen printing technology. According to simulation and experiment results, the present three-dimensional metamaterial absorber can realize an absorptivity of more than 90% in a wide band of 3.53-24.00 GHz, and improve absorbing efficiency for transverse magnetic (TM) waves of oblique incidence angle from 0° to 70°. The compression test results reveal that compressive strength of the 3D printed honeycomb can reach 10.7 MPa with density of only 254.91 kg/m³, and the energy absorption per volume W _v and per unit mass W _m are 4.37 × 10³ KJ/m³ and 17.14 KJ/Kg, respectively. The peak compressive strength and energy absorption per mass are at least 2.2 and 3 times comparing to metallic lattice cores with the same density. Outstanding electromagnetic wave absorption and mechanical performance make the present three-dimensional metamaterial absorber more competitive in engineering applications.20:T743,

	Year	Citations

References