Highly Multifunctional Performances of Boron Nitride Nanosheets/Polydimethylsiloxane Composite Foams

Abstract

Although this kind of hexagonal boron nitride (h-BN)-filled polydimethylsiloxane (PDMS) multifunctional composite foam has been greatly expected, its development is still relatively slow as a result of the limitation of synthetic challenge. In this work, a new foaming process of BNNSs-PDMS, alcohol, and water three-phase emulsion system is employed to synthesize a series of high-quality BNNSs/PDMS composite foams (BSFs) filled with highly functional and uniformly distributed BNNSs. As a result of well-bonded interfaces between the BNNSs and PDMS, enhanced multiple functions of BSFs appeared. The BSFs can show complete resilience at a compressive strain of 90% and only 3.99% irreversible deformation after 100,000 compressing–releasing hyperelastic cycles at a strain of 60%. On the basis of their outstanding shape-memory properties, the maximum voltage value of compression-driven piezo-triboelectric (CDPT) responses of the BSFs is up to ∼20 V. Depending on the remarkable super-elastic and CDPT performances, the BSFs can be used for sensitive sensing of temperature difference and electromechanical responses. Also, in the range of 12–40 GHz, the BSF materials display ultralow dielectric constants between 1.1 and 1.4 with proper dielectric loss tangent values of <0.3 and exhibit an enhanced and broadened sound adsorption capacity ranging from 500 to 6500 Hz. Although BSFs have high porosities of >65%, their thermal conductivities can still reach up to 0.407 ± 0.039 W m –1 K –1 . Moreover, the BSF materials display favorable thermal stability, obviously reduced coefficient of thermal expansion, and good flame retardancy. All of these properties render the BSFs as a new category of excellent multifunctional material.