Room temperature flash of single crystal titania: Electronic and optical properties

Abstract

Abstract A single‐crystal specimen of rutile (titania) was flashed repetitively, while increasing the electric field after each cycle. As expected, the flash onset temperature continued to drop modestly at higher fields. However, when the field was increased from 400 to 450 V cm –1 , the flashed onset fell dramatically down to room temperature. We have investigated the electrical and optical properties of this room temperature flashed specimen (called SZ). The specimen was electronically conducting. Optical absorption spectroscopy revealed a narrow band of new energy levels that were generated just below the conduction band. The gap between the conduction band and this flash‐induced energy level agreed with the peak in the electroluminescence spectrum. Optical second harmonic generation (SHG) is reported. The flash‐on condition significantly lowered the SHG, which rebounded when the flash was turned off. This result suggests that the structure becomes more centrosymmetric in the state of flash, which may represent a disordered state of defects. The possibility of studying flash behavior at room temperature, without a furnace (as in SZ type specimens), opens a considerable simplification for in‐situ characterization of flash behavior. For example, a possible relationship between memristor physics and the flash phenomenon can be studied.