Preparation of Barium Titanate–Potassium Niobate Nanostructured Ceramics with Artificial Morphotropic Phase Boundary Structure By Solvothermal Method

Abstract

Barium titanate (BaTiO3, BT)–potassium niobate (KNbO3, KN) (BT–KN) nanostructured ceramics with a distorted interface region, i.e., artificial morphotropic phase boundary (MPB) structure, were prepared by the solvothermal method. The results of the optimization of reaction conditions showed that the metastable region of only KN crystal growth was obtained using a mixture of KOH and K2CO3 as the K source and Nb2O5 as the Nb source in ethanol. Moreover, KN formation under the metastable region using a particle compact composed of a mixture of BT and Nb2O5 particles as substrates resulted in the successful preparation of BT–KN nanostructured ceramics with an artificial MPB region and a porosity of around 35%. This is the first report on the preparation of ceramics with a heteroepitaxial interface between BT and KN below 230 °C.